Effects of dentinary contamination by endodontic irrigants on bonding strength of adhesive systems

This study aimed to evaluate if 2.5% sodium hypochlorite compromises the adhesion of bonding materials. The factors in the study were the irrigation solutions in two levels: 2.5% sodium hypochlorite and saline solution; and the adhesive systems used in three levels: three-step adhesive, universal adhesive, and two-step self-etch adhesive systems. The answer variable used was the microshear bond strength obtained through a universal testing machine and fracture mode. Six groups were obtained (n=10) : Etch-and-rinse/Saline (saline solution + 3-step adhesive system - Scotchbond Multipurpose, 3M ESPE); Universal/saline (saline solution + universal adhesive system ­ Prime&Bond,); Self-etch/saline (saline solution + 2-step self-etch adhesive systems - Clearfil SE Bond); Etch-and-rinse/Hypo (sodium hypochlorite 2,5% + 3-step adhesive system - Scotchbond Multiuso); Universal/Hypo (sodium hypochlorite 2,5% + universal adhesive system ­ Prime&Bond); Self-etch/Hypo (sodium hypochlorite 2,5% + 2-step self-etch adhesive system - Clearfil Se Bond). The specimens were obtained from 60 healthy bovine incisors. The crowns were separated from the roots, and the regularization of the buccal surface was performed. The groups received saline solution and 2.5% sodium hypochlorite for 30 minutes, respectively. A matrix of 1mm and 3mm oh height was stabilized by Scotch tape to obtain the resin sticks. Afterward, the bond strength test was performed in a universal testing machine at 1mm/min speed. The data were analyzed with normality Shapiro-Wilk, two-way ANOVA, and Tukey's tests (p<0.001). Etch-and-rinse and Self-etch adhesives presented the highest bond strength values after irrigation with saline solution and 2.5% sodium hypochlorite, respectively (P < 0.01). The irrigation with 2.5% sodium hypochlorite decreased the bond strength values of Etch-and-rinse and Universal (P < 0.01). On the other hand, 2.5% sodium hypochlorite improved the bond strength values of Self-etch (P < 0.01). In conclusion, 2.5% sodium hypochlorite negatively impacted the bond strength of Etch-and-rinse and Universal but improved the adhesion of Self-etch.

Effect of alternative solvent evaporation techniques on mechanical properties of primer-adhesive mixtures / Efeito de técnicas alternativas utilizando evaporação de solvente nas propriedades mecânicas da mistura primer-adesivo

ABSTRACT This study evaluated the influence of the mode and time of solvent evaporation on the tensile strength (TS), flexural strength (FS) and elastic modulus (EM) of two adhesive systems: Scotchbond Multipurpose (SBMP) and Clearfil SE (CSEB). For this purpose, rectangular samples (2x1x7 mm) were prepared with 10 μL of primer and the solvents were evaporated with air spray at (23±1) ºC, (40±1) ºC and negative control (without spray). For each temperature, the times of 5, 20, 30, and 60 seconds were investigated. The statistical results showed that evaporation at 40±1ºC resulted in better EM for the two adhesives tested and all the evaporation times evaluated. However, there were no significant differences between the times and modes of evaporation for TS. The results of this study indicate that evaporation at a temperature of (40±1) °C could improve the elastic modulus of both adhesives tested, regardless of the evaporating time.

RESUMO Este estudo avaliou a influência do modo e do tempo de evaporação do solvente na resistência à tração (RT), resistência à flexão (RF) e módulo de elasticidade (MR) de dois sistemas adesivos: Scotchbond Multipurpose (SBMP) e Clearfil SE (CSEB). Para isso, amostras retangulares (2x1x7 mm) foram preparadas com 10 μL de primer e os solventes foram evaporados com aerossol a (23±1) ºC, (40±1) ºC e controle negativo (sem aerossol). Para cada temperatura, foram avaliados os tempos de 5, 20, 30 e 60 segundos. Os resultados estatísticos mostraram que a evaporação a (40±1) ºC resultou em melhor MR para os dois adesivos testados e todos os tempos de evaporação avaliados. No entanto, não houve diferenças significativas entre os tempos e modos de evaporação na RT. Os resultados deste estudo indicam que a evaporação a uma temperatura de (40±1) °C poderia melhorar o módulo de elasticidade de ambos os adesivos testados, independentemente do tempo de evaporação.

In-vitro comparative study of the use of 2 % chlorhexidine on microtensile bond strength of different dentin adhesives: a 6 months evaluation / Estudio comparativo in vitro del uso de clorhexidina al 2 % sobre la resistencia de unión microtensil de diferentes adhesivos dentinarios: una evaluación de 6 meses

The aim of this study was to evaluate the effect of chlorhexidine (CHX) dentin treatment on microtensile bond strength (µTBS) of adhesive systems in different storage times. Occlusal enamel was removed from ninety third-molars and flat surfaces of middle dentin were exposed. Teeth were randomly divided in 6 groups according to adhesive system (etch-and-rinse : Adper Scotchbond 1XT - ASB ; self-etch: Adper Prompt L-Pop ­ APP; and universal: Single Bond Universal - SBU) and chlorhexidine (CHX) dentin treatment (2 % CHX application for 20 s prior Primer). After resin composite build up, teeth were sectioned to obtain beam specimens and divided in 3 subgroups (n=5): 72h, 3 and 6 months storage times. After the storage times, teeth were tested in tension until failure (0.5 mm/min). SEM was performed to observe hybrid layer of adhesive systems. Data were analyzed using one-way ANOVA and Tukey tests. At 72 h, all equivalent groups (same adhesive system, different dentin treatments) maintained their µTBS when compared CHX-treatment. At 3 and 6 months, non-treated CHX groups showed less µTBS than CHX-treated ones. Six months storage time did not significantly decrease µTBS, except for G2-ASB. The effect of CHX on dentin µTBS depends on storage times and adhesive systems. While immediate µTBS was not affected by CHX treatment, CHX improved dentin µTBS after 3 and 6 months.

El objetivo de este estudio fue evaluar el efecto del tratamiento con clorhexidina (CHX) de la dentina sobre la resistencia de la unión microtensil (mTBS) de los sistemas adhesivos en diferentes tiempos de almacenamiento. Se retiró el esmalte oclusal de noventa terceros molares y se expusieron superficies planas de la dentina media. Los dientes se dividieron al azar en 6 grupos de acuerdo con el sistema adhesivo (con grabado ácido: Adper Scotchbond 1XT-ASB, auto-grabado: Adper Prompt L-Pop-APP y universal: Single Bond Universal- SBU) y el tratamiento de la dentina con clorhexidina (CHX) (aplicación de CHX al 2 % 20 s antes del Primer). Después de la aplicación de la resina compuesta, los dientes fueron seccionados para obtener muestras en forma de barras y divididos en 3 subgrupos (n = 5) con tiempos de almacenamiento de 72 h, 3 y 6 meses. Después de los tiempos de almacenamiento, los dientes se sometieron a tensión hasta la fractura (0,5 mm / min). SEM se realizó para observar la capa híbrida de sistemas adhesivos. Los datos se analizaron mediante ANOVA unidireccional y pruebas de Tukey. A las 72 h, todos los grupos equivalentes (el mismo sistema adhesivo, diferentes tratamientos de dentina) mantuvieron su mTBS cuando se comparó el tratamiento CHX. A los 3 y 6 meses, los grupos CHX no tratados mostraron menos mTBS que los tratados con CHX. Seis meses de tiempo de almacenamiento no disminuyó significativamente el mTBS, excepto para el G2-ASB. El efecto de CHX sobre la dentina mTBS depende del tiempo de almacenamiento y de los sistemas adhesivos. Mientras que el mTBS inmediato no se vio afectado por el tratamiento con CHX, CHX mejoró la mTBS a dentina después de 3 y 6 meses.

Influence of the passive evaporation of adhesive on the conductance of dentin

ABSTRACT: Aim: Determine the influence of time of passive evaporation of the solvent in a universal adhesive on the hydraulic conductance and permeability of dentin in an ex vivo human model. Henceforth, 60 healthy non-occluding third molars, indicated for therapeutic extraction/removal, of informed and consented patients aged between 18 and 30 years, were used here in. First, extracted teeth were incorporated into epoxy resin blocks and then dentin disks (1mm +/- 0.1 mm thick) were prepared. Dentin was acid etched with 35% ortho-phosphoric acid for 15 seconds in order to remove the smear layer and obtain permeable dentin. Samples were then randomized and divided into 5 groups (n=12). A Single Bond Universal adhesive layer with different time of passive evaporation of the solvent was then applied: GC=10 seconds, G1=30 seconds, G2=60 seconds, G3=300 seconds and G4=50 minutes. Finally, the flow rate was measured using a diffusion chamber, a model previously proposed by Pashley et al. Results: The obtained hydraulic conductance averages were as follows: GC=0.00052, G1=0.00018, G2=0.00006, G3=0.00005, G4=0.00005 expressed in uL•cm-2•min-1cm•H2O-1. For comparisons between groups, ANOVA and post hoc Tukey (ρ<0.05) tests were applied, resulting in a statistically significant difference between the GC group and all experimental groups (ρ <0.05). An influence of solvent passive evaporation thereby reducing hydraulic conductance in the experimental groups, was detected.

Comparative study on direct and indirect bracket bonding techniques regarding time length and bracket detachment

OBJECTIVE: The aim of this study was to assess the time spent for direct (DBB - direct bracket bonding) and indirect (IBB - indirect bracket bonding) bracket bonding techniques. The time length of laboratorial (IBB) and clinical steps (DBB and IBB) as well as the prevalence of loose bracket after a 24-week follow-up were evaluated. METHODS: Seventeen patients (7 men and 10 women) with a mean age of 21 years, requiring orthodontic treatment were selected for this study. A total of 304 brackets were used (151 DBB and 153 IBB). The same bracket type and bonding material were used in both groups. Data were submitted to statistical analysis by Wilcoxon non-parametric test at 5% level of significance. RESULTS: Considering the total time length, the IBB technique was more time-consuming than the DBB (p < 0.001). However, considering only the clinical phase, the IBB took less time than the DBB (p < 0.001). There was no significant difference (p = 0.910) for the time spent during laboratorial positioning of the brackets and clinical session for IBB in comparison to the clinical procedure for DBB. Additionally, no difference was found as for the prevalence of loose bracket between both groups. CONCLUSION: the IBB can be suggested as a valid clinical procedure since the clinical session was faster and the total time spent for laboratorial positioning of the brackets and clinical procedure was similar to that of DBB. In addition, both approaches resulted in similar frequency of loose bracket.

OBJETIVO: avaliar o tempo necessário para realização da colagem de braquetes pelas técnicas direta (CDB) e indireta (CIB), mensurando o tempo despendido entre a parte laboratorial (CIB) e a parte clínica (CDB e CIB), e a prevalência de descolamentos durante o período de observação de 24 semanas. MÉTODOS: dezessete pacientes (7 homens e 10 mulheres), com idade média de 21 anos, com necessidade de tratamento ortodôntico, foram selecionados para participar desse estudo. Foram utilizados um total de 304 braquetes, sendo que 151 foram colados pela técnica de CDB e 153 pela CIB, com o mesmo tipo de braquete e material de colagem. Os dados foram submetidos ao teste não paramétrico de Wilcoxon, com significância de 5%. RESULTADOS: o tempo total para realização da CIB foi maior em relação à CDB (p < 0,001). Levando em consideração apenas a fase clínica, foi observado que o tempo para CIB foi menor em relação a CDB (p < 0,001). A comparação entre o tempo despendido para o posicionamento dos braquetes em laboratório mais o tempo em clínica para CIB com o tempo em clínica para a CDB revelou que não houve diferença significativa (p = 0,910), nem tampouco quanto à prevalência de descolamento dos braquetes. CONCLUSÃO: a CIB apresenta-se como uma utilidade clínica singular, pois o tempo em clínica foi menor que o da CDB. O tempo despendido no posicionamento dos braquetes no laboratório e de execução clínica da CIB foi semelhante ao tempo gasto pela CDB, a quantidade de descolamentos foi semelhante entre as técnicas.

Avaliação da influência da técnica incremental na força coesiva de diferentes resinas compostas / Influence of incremental technique on the cohesive strength of different dental resin composites: microtensile bond strenght analysis

O objetivo desse estudo foi avaliar a influência da técnica incremental na força coesiva de diferentes resinas compostas. Foi confeccionado para este trabalho um dispositivo bipartido de Teflon que se encaixa em um magazine metálico para manter as metades em posição durante a preparação dos corpos de prova do compósito. A partir deste dispositivo de forma cônica, e dimensões: 4mm de base, 2mm de diâmetro na interface e 4mm de altura, foram obtidos 120 espécimes, divididos em 12 grupos ( n=10), 6 grupos sem o uso de adesivo e 6 grupos com o uso de adesivo. Foram utilizadas as resinas compostas: Filtek P90-3M ESPE, St.Paul,MN,USA e Filtek Z350 XT-3M ESPE, St. Paul, MN,USA , ambas na cor A3, inseridas no dispositivo bipartido de teflon segundo a técnica incremental adotada, técnica incremental obliqua, horizontal ou incremento único. A resina foi inserida com uma espátula metálica em incrementos horizontais ou em incrementos oblíquos, conforme a inclinação dada pelo instrumental utilizado, em incrementos de 2mm de espessura, ou ainda inserida de uma só vez, em porção única de 4mm de espessura e fotoativadas por 20 segundos, segundo indicação do fabricante. Os espécimes foram submetidos aos testes de tração para avaliar a força coesiva da resina composta e a influência da técnica incremental utilizada. Os dados obtidos foram analisados quanto à sua distribuição, à Análise de Variância (ANOVA) e ao Teste de Tukey HSD (p>0,05 %). Pode - se concluir que a técnica incremental utilizando incrementos oblíquos influencia negativamente na resistência coesiva. A Resina Filtek Z350XT possui maior resistência coesiva quando comparada à resina Filtek P90. A utilização de adesivo influencia negativamente na resistência coesiva.

The aim of this study was to evaluate the influence of incremental technique on the cohesive strength of different dental resin composites. A total of 120 conical specimens of different resin composites, Filtek P90 and Filtek Z350 XT, both in color A3, were made in a bipartite teflon device with the following dimensions: 4 mm base diameter of 2mm and 8mm in height. The specimens were assigned into 12 groups (n = 10), 6 groups without the use of adhesive and 6 groups with the use of adhesive. The cavity was filled with a metal spatula in oblique or horizontal increments of 2mm thick or inserted at once in one portion 4mm thick and each increment was light-cured for 20 seconds following manufactures instructions. The specimens were subjected to microtensile tests to evaluate the cohesive strength of the resin composite and the influence of incremental technique used. Data were submitted to ANOVA and Tukey's HSD test (p<0,05%).Can be concluded that the incremental technique using increments oblique negatively influence the cohesive strength. The resin Filtek Z350XT has greater cohesive resistance when compared to Filtek P90. The use of adhesive negatively influence the cohesive resistance

Bond strength between acrylic resin and maxillofacial silicone

The development of implant dentistry improved the possibilities of rehabilitation with maxillofacial prosthesis. However, clinically it is difficult to bond the silicone to the attachment system. OBJECTIVES: This study aimed to evaluate the effect of an adhesive system on the bond strength between acrylic resin and facial silicone. MATERIAL AND METHODS: A total of 120 samples were fabricated with auto-polymerized acrylic resin and MDX 4-4210 facial silicone. Both materials were bonded through mechanical retentions and/or application of primers (DC 1205 primer and Sofreliner primer S) and adhesive (Silastic Medical Adhesive Type A) or not (control group). Samples were divided into 12 groups according to the method used to attach the silicone to the acrylic resin. All samples were subjected to a T-peel test in a universal testing machine. Failures were classified as adhesive, cohesive or mixed. The data were evaluated by the analysis of variance (ANOVA) and the Tukey's HSD test (α=.05). RESULTS: The highest bond strength values (5.95 N/mm; 3.07 N/mm; 4.75 N/mm) were recorded for the samples that received a Sofreliner primer application. These values were significantly higher when the samples had no scratches and did not receive the application of Silastic Medical Adhesive Type A. CONCLUSIONS: The most common type of failure was adhesive. The use of Sofreliner primer increased the bond strength between the auto-polymerized acrylic resin and the Silastic MDX 4-4210 facial silicone.

Formulation and evaluation of ficus glomerata mucilage sustained release matrix tablets of gliclazide

The main aim of present investigation was to develop sustained release matrix tablets of Gliclazide using fruit mucilage from the plant Ficus glomerata. Varying ratios of drug and polymer viz. 1:0.25, 1:0.5, 1:0.75, 1:1.0 and 1:1.25 were selected for the study. The flow properties of powdered mucilage and physical properties of matrix tablets were performed. The swelling behavior and release rate characteristics were studied. The in vitro drug release data was analyzed by zero order, first order, Higuchi plot, Peppas plot and Hixon-Crowell Models. It was observed that as the proportion of mucilage increased the release of drug from the matrix tablets was retarded. Stability studies were conducted at 40 +/- 2°C and RH 75 +/- 5% for 3 months indicates that Gliclazide was stable in the matrix tablets. The Differential Scanning Calorimetric [DSC] and Fourier Transform Infrared [FTIR] study revealed that there was no negative chemical interaction between drug and the mucilage used. From the dissolution study, it was concluded that dried Ficus glomerata mucilage can be used as an excipient for making sustained release matrix tablets

Effect of an additional hydrophilic versus hydrophobic coat on the quality of dentinal sealing provided by two-step etchand-rinse adhesives

OBJECTIVE: To test the hypothesis that the quality of the dentinal sealing provided by two-step etch-and-rinse adhesives cannot be altered by the addition of an extra layer of the respective adhesive or the application of a more hydrophobic, non-solvated resin. MATERIAL AND METHODS: full-crown preparations were acid-etched with phosphoric acid for 15 s and bonded with Adper Single Bond (3M ESPE), Excite DSC (Ivoclar/Vivadent) or Prime & Bond NT (Dentsply). The adhesives were used according to the manufacturers' instructions (control groups) or after application to dentin they were a) covered with an extra coat of each respective system or b) coated with a non-solvated bonding agent (Adper Scotchbond Multi-Purpose Adhesive, 3M ESPE). Fluid flow rate was measured before and after dentin surfaces were acid-etched and bonded with adhesives. RESULTS: None of the adhesives or experimental treatments was capable to block completely the fluid transudation across the treated dentin. Application of an extra coat of the adhesive did not reduce the fluid flow rate of adhesive-bonded dentin (p>0.05). Conversely, the application of a more hydrophobic non-solvated resin resulted in significant reductions in the fluid flow rate (p<0.05) for all tested adhesives. CONCLUSIONS: The quality of the dentinal sealing provided by etch-and-rinse adhesives can be significantly improved by the application of a more hydrophobic, non-solvated bonding agent.

The knowledge and attitude of general dentists toward denture adhesives in Tehran.

Background: The purpose of this study was to generate discussion and communication among a group of general dentists in Tehran on their viewpoints regarding denture adhesives. Have they accepted denture adhesive as a material to enhance denture retention, stability and function? Materials and Methods: In the summer of 2007, a questionnaire was mailed to 300 general dentists who were assigned with a random systematic sampling method from general dentists in Tehran. The questions were arranged in two parts of evaluating knowledge and attitude. In evaluation of knowledge, dentists were classified into groups of good, moderate, weak and lack of knowledge. In evaluation of attitude, dentists were classified into positive, moderate and negative groups. (Evaluating attitude was carried out in good and moderate groups of knowledge.) Results: The study showed that 14%, 32% and 37% of the general dentists had respectively good, moderate and weak knowledge toward denture adhesive while 16.3% had no knowledge about this material. In evaluation of attitude through dentists with positive and moderate knowledge toward denture adhesive, 9.3%, 71.3% and 19.4% had respectively positive, moderate and negative attitude toward denture adhesive. The c2 test showed a significant statistical relation between situation of knowledge and experiences of dentists. Discussion: This study demonstrated that the rate of knowledge of these 300 general dentists in Tehran towards denture adhesives has not been in a good situation. It is believed that denture adhesive be able to enhance the fitness of a denture and provide psychological relief to the patient. Dentists agreed that education, not only for practitioners but also for patients, would raise the advantageous features and reduce the misuse of denture adhesive. Education of the topic "Denture adhesive" should be more concerned in dental universities.

Degree of conversion of adhesive systems light-cured by LED and halogen light

This study evaluated the effect of blue light emitting diode (LED) and quartz tungsten halogen (QTH) on the degree of conversion (DC) of an etch-and-rinse Single Bond adhesive system (SB) and a mixture composed of primer solution and resin bond from Clearfil SE Bond self-etching adhesive system (CB) using Fourier transform infrared analysis (FTIR). Adhesives were applied to potassium bromide pellet surfaces and FTIR analyses were performed before and after photo-activation for 10 s with either LED (Freelight 1 - 400 mw/cm²) or QTH (XL 3000 - 630 mw/cm²) light-curing units (n=8). Additional FTIR spectra were obtained from photo-activated samples stored in distilled water for 1 week. The DC was calculated by comparing the spectra obtained from adhesive resins before and after photo-activation. The results were analyzed by two-way split-plot ANOVA and Tukey's test (p<0.05). Both adhesive systems exhibited low DC ( percent) immediately after photo-activation (SB/QTH: 18.7 ± 3.9; SB/LED: 13.5 ± 3.3; CF/QTH: 13.6 ± 1.9; CF/LED: 6.1 ± 1.0). The DC of samples light-cured with LED was lower than DC of those light-cured with QTH, immediately after light curing and after 1 week (SB/QTH: 51.3 ± 6.6; SB/LED: 50.3 ± 4.8; CF/QTH: 56.5 ± 2.9; CF/LED: 49.2 ± 4.9). The LED curing unit used to photo-activate the adhesive resins promoted lower DC than the QTH curing unit both immediately after light curing and 1 week after storage in water.

Este estudo avaliou a influência de sistemas de fotoativação no grau de conversão (GC) de sistemas adesivos por meio da análise infravermelha transformada de Fourier (FTIR). Os sistemas adesivos Single Bond (SB) e Clearfil SE Bond (CF) foram aplicados em pastilhas de brometo de potássio e fotoativados com luz halógena (XL 3000 - 630 mw/cm²) (QTH) e LED (Elipar Freelight 1 - 400 mw/cm²) por 10 s (n=8). Foram obtidos espectros de FTIR antes e imediatamente após a fotoativação, e tambem após 1 semana de armazenamento em água destilada. Calculou-se o GC comparando-se a razão entre os picos das bandas dos espectros, antes e após a fotoativação. Os resultados de GC foram submetidos à ANOVA e ao teste de Tukey (p<0,05). Para ambos os sistemas adesivos, o GC ( por cento) obtido imediatamente após a fotoativação com LED foi inferior ao obtido utilizando-se QTH (SB/QTH: 18,7 ± 3,9; SB/LED: 13,5 ± 3,3; CF/QTH: 13,6 ± 1,9; CF/LED: 6,1 ± 1,0). Após uma semana foi observado um aumento significativo no GC de todos os grupos, porém os valores dos grupos fotoativados com LED mantiveram-se inferiores aos obtidos com QTH (SB/QTH: 51,3 ± 6,6; SB/LED: 50,3 ± 4,8; CF/QTH: 56,5 ± 2,9; CF/LED: 49,2 ± 4,9). O GC dos adesivos fotoativados com LED foi inferior ao observado após fotoativação com QTH, imediatamente após fotoativação como após 1 semana de armazenamento em água.

Effect of dentinal surface preparation on bond strength of self-etching adhesive systems

O objetivo deste estudo foi avaliar os efeitos de tratamentos superficiais da dentina na resistência de união (RU) de dois sistemas adesivos autocondicionantes, Clearfil SE Bond (CSE) e One-Up Bond F (OUB). Superfícies dentinárias planificadas de vinte e quatro terceiros molares foram preparadas com pontas diamantadas em alta rotação, brocas "carbide" em baixa rotação ou abrasionadas com lixas de SiC (#600). Os adesivos foram aplicados e fotoativados de acordo com as instruções dos fabricantes. Um bloco de compósito foi construído nas superfícies tratadas e cada incremento de resina foi fotoativado por 40 segundos. Após armazenamento em água (37°C/24 h), os dentes restaurados foram serialmente seccionados paralelamente ao seu longo eixo para obtenção de espécimes com área de secção transversal de aproximadamente 0,8 mm2 (n = 20). Os espécimes foram testados em máquina universal de ensaios (0,5 mm/min). A área de união foi mensurada e os resultados (MPa) foram analisados pela ANOVA (2 fatores) e pelo teste de Tukey (p < 0,05). Os grupos restaurados com o adesivo CSE mostraram os maiores valores de RU para todos os tratamentos. A superfície da dentina preparada com brocas carbide em baixa rotação reduziu a RU para o adesivo CSE; entretanto, a RU do adesivo OUB não foi afetada pelos tratamentos. O efeito da preparação da dentina na RU foi material-dependente.

Morphological characterization of the tooth/adhesive interface

The purpose of this study was to assess the morphological characteristics of the tooth/adhesive interface using different adhesive systems in MOD restorations under scanning electron microscopy (SEM). The tested hypothesis was that the morphology of the bonding interface would vary in different areas of MOD restorations for the three adhesive systems. MOD cavities were prepared in 12 sound extracted human third molars and restored with Filtek Z250 composite resin and one of the following adhesive systems: Experimental ABF (n=4), Clearfil SE Bond (n=4) self-etching primers and Single Bond etch-and-rinse adhesive system (n=4). After 24-h storage in distilled water at 37°C, teeth were sectioned and prepared for SEM. The interfacial morphology varied depending on the adhesive system and also on the evaluated area. The null hypothesis was accepted because the morphology of the tooth/adhesive interface reflected the characteristics of both the dental substrate and the adhesive systems.

Este estudo teve o objetivo de observar a morfologia da interface dente-restauração de diferentes sistemas adesivos em cavidades MOD, por microscopia eletrônica de varredura (MEV). A hipótese do estudo foi de que a morfologia da interface adesiva poderia variar nas diferentes regiões da cavidade MOD, para algum dos 3 sistemas adesivos estudados. Preparos tipo MOD foram confeccionados em 12 terceiros molares humanos hígidos e restaurados com resina composta Filtek Z250 e os seguintes sistemas adesivos: ABF (n=4), Clearfil SE Bond (n=4) (sistemas adesivos autocondicionantes) e Single Bond (n=4) (sistema adesivo de condicionamento ácido total). Após 24 h de armazenamento em água destilada a 37°C, os dentes foram secionados e preparados para MEV. A morfologia da interface de união variou com o sistema adesivo e com a região analisada. A hipótese do estudo foi aceita, pois a morfologia da interface de união refletiu as características do substrato dental e dos sistemas adesivos testados.

Shear bond strength of acetone-based one-bottle adhesive systems

O objetivo deste estudo foi avaliar a resistência ao cisalhamento de quatro sistemas adesivos de frasco único com solvente acetona e um sistema com solvente etanol em esmalte e à dentina. Cinqüenta molares humanos foram seccionados ao meio no sentido mesiodistal e incluídos com resina acrílica em tubos de PVC. As superfícies vestibulares foram desgastadas até atingir dentina plana, enquanto as superfícies linguais foram desgastadas até atingir esmalte plano. Os espécimes foram polidos até lixa d'água de granulação 600 e divididos aleatoriamente entre os 5 grupos (n=20; 10 espécimes de dentina e 10 espécimes de esmalte), de acordo com o sistema adesivo utilizado: One-Step (Bisco); Gluma One Bond (Heraeus Kulzer), Solobond M (Voco), TenureQuik w/F (Den-Mat) and OptiBond Solo Plus (Kerr) (controle). Os adesivos foram aplicados conforme as instruções dos fabricantes. Uma cápsula cilíndrica gelatinosa (d=4,5mm), preenchida com compósito híbrido de cada fabricante foi posicionada sobre a superfície dental e fotopolimerizada durante 40 s. Após 24 h, os corpos-de-prova foram submetidos a ensaios de cisalhamento em uma máquina de ensaios Instron com velocidade de 5 mm/min. Os dados foram analisados estatisticamente pela ANOVA a um critério e teste de Duncan post hoc (p£0.05). As médias de resistência ao cisalhamento resistência em esmalte e dentina (MPa) (±SD) foram: Esmalte: One-Step=11,3(±4,9); Gluma One Bond=16,3(±10,1); Solobond M=18,9(±4,5); TenureQuik w/F=18,7(±4,5) e OptiBond Solo Plus=16,4(±3,9); Dentina: One-Step=6,4(±2,8); Gluma One Bond=3,0(±3,4); Solobond M=10,6(±4,9); TenureQuik w/F=7,8(±3,9) e OptiBond Solo Plus=15,1(±8,9). Em esmalte, todos os agentes adesivos tiveram resultados estatisticamente semelhantes entre si (p>0.05). Entretanto, em dentina, o sistema adesivo a base de etanol apresentou maior resistência de união que todos os sistemas a base de acetona (p£0.0001). O tipo de solvente presente nos sistemas adesivos de frasco único não exerceu influência na sua capacidade de união ao esmalte, mas se mostrou um componente importante na adesão dentinária, o que deve ser levado em conta quando da escolha de um sistema adesivo.

One-bottle adhesives: in vitro analysis of solvent volatilization and sealing ability

O objetivo deste estudo foi comparar a taxa de volatilização do solvente e a capacidade de selamento de diferentes adesivos de frasco único que estavam em constante uso clínico – um à base de etanol/água (Single Bond, 3M/ESPE) e um à base de acetona (Prime & Bond 2.1, Dentsply/Caulk). Nove frascos de cada agente foram coletados das clínicas da faculdade e outros novos foram utilizados como controle. Os pesos de todos os frascos e de frascos vazios foram determinados em uma balança analítica. Uma gota de cada solução foi dispensada na balança, tomando-se seu peso inicial (PI) e, após 10 min, seu peso final (PF). A razão PI/PF foi utilizada para determinar a taxa de volatilização do solvente. Os frascos com os maiores níveis de evaporação (SB Controle e PB Controle) e com os menores níveis de evaporação (SB Teste e PB Teste) foram aplicados em restaurações Classe V com margens em dentina. Os espécimes foram termociclados e imersos em solução de fucsina básica a 0,5%. A penetração do corante foi avaliada sob magnificação e os dados foram submetidos ao teste de Kruskal-Wallis. A volatilização do solvente foi mais rápida para o adesivo à base de acetona. As razões PI/PF variaram de 1,239 a 1,515 para SB e de 3,488 a 6,476 para PB. PB-Controle e SB-Controle exibiram vedamento similar. Os maiores escores de penetração foram encontrados para o PB-Teste (p < 0,05). Os resultados indicam que a habilidade de selamento pode ser afetada pela repetida utilização dos frascos de adesivo à base de acetona.

Effect of microwave treatments on dimensional accuracy of maxillary acrylic resin denture base

A energia por microondas tem sido utilizada como um método alternativo para desinfecção e esterilização de próteses dentárias. Neste estudo, foi avaliada a influência do tratamento com energia de microondas na precisão de adaptação de bases de próteses totais superiores. Trinta bases acrílicas (3 mm de espessura) foram confeccionadas sobre modelos de gesso pela técnica de rotina, utilizando a resina acrílica Clássico. Após a polimerização e resfriamento, foram demufladas e armazenadas em água destilada por 30 dias. Ao final deste período, as bases foram divididas em três grupos: grupo I (controle; sem desinfecção); grupo II tratamento em microondas por 3 min a 500 W; e grupo III tratamento por 10 min a 604 W. Em seguida, as bases foram fixadas em seus respectivos modelos de gesso com cola instantânea (Super Bonder), e os conjuntos modelo/base foram seccionados na região palatina posterior. Os desajustes entre as bases e os modelos foram verificados com auxílio de um microscópio comparador linear em cinco pontos. Não houve diferença estatisticamente significante quanto à adaptação das bases entre o grupo I e o grupo II. Contudo, o grupo III apresentou as maiores discrepâncias, diferindo estatisticamente quando comparado aos demais grupos (p<0.05). O tratamento com energia de microondas utilizando ciclo de 10 min a 604 W, promoveu as maiores discrepâncias na adaptação das bases acrílicas de próteses totais superiores aos modelos de gesso.

Comparative evaluation of tensile bond strength of denture base resins to surface pretreated cobalt chromium base metal alloys--an in vitro study.

This study was undertaken to evaluate the tensile bond strength of acrylic resins to surface pretreated Cobalt-chromium base metal alloy. A total of 60 tensile bar specimens were prepared. One half of the bar was cast in cobalt-chromium alloy and the other half made of denture base resins attached to the alloy following surface pretreatment. Two denture base resins and five surface pre-treatments were used which included sandblasting, acid etching, use of metal adhesive primers and the combination of the above mentioned modes. Gradual axial loads were applied on the tensile bar specimen mounted on a Hounsfield tensometer till bond failure was evident. Statistical evaluation was done using Mann-Whitney U test. The study results indicate that the bond strength in those specimens wherein a combination of sandblasting, acid etching and priming was done as surface pretreatment, showed the maximum values as compared to the other groups.

Comportamiento biomecánico de tres cementos de ionómero-resina utilizados para cementar pernos intrarradiculares. Un ensayo "in vitro" / Biomechanical behavior or three glass ionomer-resin cements used for cementing intraradicular posts. An in vitro assay

El objetivo de este trabajo fue evaluar "in vitro" el efecto de los posibles cambios volumétricos desarrollados por los ionómeros vítreos híbridos, cuando son utilizados para cementar pernos intrarradiculares. Se realizaron dos ensayos diferentes: en el ensayo No.1 se utilizaron 20 raíces de vidrio con un espesor de pared de 1 mm., contenidas dentro de tacos cilídricos de acrílico y unidas a ellos por medio de una silicona de mediana viscosidad. En el interior de las raíces se cementaron tornillos que no ejercían ningún tipo de presión, utilizando para ello tres diferentes cementos de ionómero-resina y un cemento de fosfato de cinc (control). Los especímenes fueron sometidos durante 90 días a una carga compresiva de 150 N en un medio acuoso mantenido a temperatura constante de 37 grados C. En el ensayo No.2 se utilizaron los mismos procedimientos experimentales, pero en este caso las raíces presentaban un espesor de pared de 2 mm. En todos los especímenes pertenecientes al ensayo No.1 se verificó la presencia de diferentes grados de fractura: microfracturas escasas y espaciadas en la masa de los cementos (más frecuentes y pronunciadas en la masa de fosfato de cinc) y fracturas totales en las paredes de las raíces artificiales de vidrio. En el ensayo No.2, las paredes de las raíces se encontraban intactas en todos los casos, aunque sí se produjeron microfracturas en la masa de los cementos, las que nuevamente fueron más frecuentes y pronunciadas en el cemento de fosfato de cinc. Los resultados sugieren que el factor determinante en la producción de fracturas en las paredes de las raíces artificiales de vidrio del ensayo No.1 parecería depender del espesor y la resistencia de las mismas y no de los posibles cambios volumétricos ocurridos en la masa de los cementos testeados